Chemical properties
Quartz glass is acidic materials, except hydrofluoric acid and hot phosphoric acid, on any other acids were shown to be inert, is the best anti acid materials. At room temperature, alkali and salt on quartz glass corrosion degree isminimal, so do not rule out in these reagents are used in the quartz glass.
Transparent quartz glass than opaque quartz glass has better chemical stability, this is because the latter becausethe bubbles exposed to corrosive liquid superficial area has increased by.
A variety of solution weight loss of quartz glass | |||||
Solution name |
Density (比重) |
(℃) |
Etching time( 小時(shí)) |
Loss of weight (g/㎡) |
|
Transparent quartz glass | Opaque quartz glass | ||||
Hydrochloric acid | 1.19 | 60 | 24 | 0.031 | 0.16 |
Nitric acid | 1.40 | 115 | 24 | 0.11 | 0.15 |
Sulfuric acid | 1.84 | 205 | 24 | 0.06 | 0.13 |
Hydrofluoric acid | 38% |
室溫 (22℃) |
2 | 259.39 | 379.80 |
Phosphoric acid | -- | 200 | 15 | 微量 | -- |
-- | 300 | 15 | 58.00 | -- | |
Sodium hydroxide | 1% | 101 | 2 | 0.80 | 5.15 |
Sodium hydroxide | 1% | 98< | 2 | 0.68 | 4.63 |
Ammonium hydroxide | 25% | 65 | 2 | 0.09 | 0.33 |
Sodium chloride | 10% | 102 | 2 | 0.14 | 0.34 |
Sodium carbonate | 10% | 102 | 2 | 1.20 | 4.99 |
Electrical properties
Quartz glass with high dielectric strength and very low electrical conductivity, is in high temperature, high pressureand high frequency, can still maintain high dielectric strength and resistance, in the band hardly dielectric loss, thereforethe quartz glass is an excellent high temperature dielectric insulating material.
Quartz glass electric energy | ||||
Property name | Electrical performance index | Species | Transparent quartz glass | Opaque quartz glass |
Breakdown voltage (1000 volts / mm ) | 溫室 >30 | 溫室 >16 | ||
500℃ 11 | 7.6 | |||
Dielectric constant (10^6) | ε=3.7 | ε=3.5 | ||
Dielectric loss TG (50cycles / second ) | 0.0003 | 0.001 | ||
Resistance ( ohm cm ) | 20℃ 10^-18 | 10^-16 |
Optical properties of
Quartz glass optical performance has its one's own knack in, it can be through the Far Ultraviolet Spectroscopic, is all ultraviolet permeable material the best, but also through the visible and near infrared spectroscopy. According to the requirements of users, from 185-3500mμband within arbitrary selection of the desired species. As the quartz glasshigh temperature, thermal expansion coefficient is extremely small, chemical thermal stability is good, bubble, stripes,uniformity, birefringence can be comparable with general optical glass, so it is in the work under various bad situationsis of high stability optical system the essential optical materials.
Optical quartz glass refractive index |
||
Wave length ( nm ) |
Crystal melting Quartz glass |
Synthesis Quartz glass |
185.41 193.53 202.54 206.20 213.85 214.45 226.50 232.94 237.83 248.20 250.20 257.62 265.36 274.87 280.35 289.36 298.06 307.59 313.17 328.36 334.15 340.36 346.69 361.17 365.48 398.84 404.65 435.83 486.13 546.07 587.56 656.27 |
1.57464 1.56071 1.54729 1.54269 -- 1.53385 1.52318 1.51834 -- -- 1.50762 1.50397 -- 1.49634 -- -- 1.48859 -- -- 1.48183 -- 1.47877 1.47766 1.47513 -- 1.47028 -- 1.46679 1.46324 1.46021 1.45857 1.45646 |
-- -- 1.54717 1.54266 1.53434 -- 1.52299 -- 1.51473 1.50841 -- 1.50351 1.49994 -- 1.49403 1.49098 1.48837 1.48575 1.48433 -- 1.47976 1.47860 1.47748 1.47503 1.47448 -- 1.46961 1.46669 1.46314 1.46007 1.45847 1.45637 |
Note: measurement error:±3×10^-5 |
Quartz glass structure, impurity content, OH gene and NO, CO content is the main factor affecting the spectral transmittance, atoms of oxygen combined with malnutrition in0.24 μoffice has absorption peak, containing OH groupsof quartz glass, in2.7 μoffice due to molecular vibrations will produce obvious absorption peak, UV transmittancemainly due to metal impurities caused by atomic absorption spectrometry.
Optical quartz glass refractive index |
|||
Wavelength ( microns ) |
Index of refraction |
Wavelength ( microns ) |
Index of refraction |
0.67 0.68 0.69 0.70 0.80 0.90 1.00 1.10 1.20 2.20 2.30 2.40 2.50 2.60 2.70 2.80 |
1.456066 1.455818 1.455579 1.455347 1.453371 1.451808 1.450473 1.440261 1.448110 1.435111 1.433462 1.431730 1.429911 1.428001 1.425995 1.423891 |
1.30 1.40 1.50 1.60 1.70 1.80 1.90 2.00 2.10 2.90 3.00 3.10 3.20 3.30 3.40 3.50 |
1.446980 1.445845 1.444687 1.443492 1.442250 1.440954 1.439957 1.438174 1.436680 1.421684 1.41937 1.41694 1.41440 1.41173 1.40893 1.40601 |
The spectral characteristic curves of quartz glass
Fused quartz glass is well infrared transparent materials, but due to the existence of impurities, UV transmittance.Oxyhydrogen melting crystal obtained quartz glass, due to oxygen defects of structure, in0.24 μa peak, while containing OH groups, so the infrared transmission is extremely low. Synthetic raw material gas refining high purity quartz glass is the best ultraviolet permeable material, but in 2.7μwith severe OH absorption peak. Only with the synthetic raw materials through the fused with or without hydrogen flame melting into optical quartz glass, can very well through thefar ultraviolet to near infrared continuous spectrum.
Quartz glass optical constants |
||
Project / index / variety |
Crystal melting Quartz glass |
Synthesis Quartz glass |
Nd(He587.56mμ) Nf(H486.13mμ) Nc(H656.27mμ) |
1.45857 1.46324 1.45646 |
1.4587 1.46314 1.45637 |
Coefficient of dispersion V=(Nd-1)/(Nf-Nc) Central dispersion: Nf-Nc |
67.6 0.00678 |
67.7 0.00677 |
| 特级做A爱片免费69 两性伦乱激情免费视频 | 又大又粗又黄的视频 | 潘金莲一级婬片AAA 91丨九色丨熟女高潮 | 欧美成人一区二区三区片免费 | 特级太黄A片老妇A片 | 外国AV无码在线观看 | 亚洲精品污一区二区三区 | 国产寡妇婬乱A片AAAA片下载 | 亚洲日本苍井空精品偷拍无码制服 | 3D精品啪啪一区二区免费 | 丝袜熟女脚交足在线一区 | 91精品无码久久久久久五月天 | 变态小说之国产激情网 | 国产精品十八禁久久久久久白浆 | 含羞草aⅴ国产精品今日更新 | 亚洲精品秘 一区二区三区蜜桃久 | 色欲合久久久无码中文字幕波多蜜桃 | 亚洲精品成人a v无码A片午夜 | 无码人区久久一区二区三区69 | 成人A片无码专区精品爆乳APP | 黄的在线看的视频网站 | 国产的级特黄AAA片做受什 | 免费人妻AV无码专区 | 天天日天天干天天插1 | 久久精品黄AA片一区二区三区 | 国产91 丝袜在线播放00 | 四川妇BBw搡BBB搡BBB | 一级女性全黄久久生活片免费 | 国产精品秘 一区二区入口九绯色 | 国产AV中文字字幕乱码天堂庄园 | 色噜噜狠狠一区二区三区果冻 | 国产婬乱片A片AAA毛片下载 | 在线观看美女洗澡青青草 | 又大又粗又硬又黄的视频 | 无码人妻一区二区三区四区老鸭窝 | 欧美成人A片Ⅴ一区二区三区动漫 | 国产熟女白浆精品视频2 | 国产一级婬片A片久久久网站入口 | 熟女人妻一区二区三区 | 国产91在线拍揄自揄拍无码九色 |